X80钢在含有SRB的海水溶液中阴极保护准则适用性

丁清苗¹, 范玥铭¹, 张迎芳²

作者信息 +

Study on the cathodic protection criteria applicability of X80 steel in seawater solution containing SRB

DING Qing-miao¹, FAN Yue-ming¹, ZHANG Ying-fang²

Author information +

文章历史 +

摘要

通过表面观察及电化学方法研究X80钢在含有SRB的海水溶液中阴极保护准则的适用性,测试结果表明:腐蚀控制因素为阳极控制,对金属施加阴极极化第5天降低金属腐蚀速度主要通过增大金属表面SRB的附着电阻和电荷转移电阻实现;而施加阴极极化第10天,阴极保护主要通过改变金属表面电荷转移电阻控制腐蚀速度,且阴极极化电位越大控制效果越好。无阴级保护的金属试样腐蚀产物较多且附着力差,施加阴极保护的金属试样腐蚀产物较少且附着力较强。阴极保护的确能对存在SRB的海水溶液环境中X80钢起到阴极极化作用,但极化5 d时传统的阴极保护准则中-850 mV_CSE(即-770 mV_SCE)电位未达到85%的保护要求,-950 mV_CSE(即-870 mV_SCE)电位刚刚能满足保护要求;而极化10 d时2种极化电位下保护度都有所下降且都不能满足保护要求,因此还需要进一步实验确定其合适的阴极保护电位。

Abstract

The applicability of cathodic protection criteria was studied by surface observation and electrochemical method while the X80 steel was immersed into seawater solution containing SRB. The results revealed:The corrosion was anode control. The corrosion rate was reduced by increasing the SRB adhesion resistance and the charge transfer resistance on the metal surface in the fifth day. While the metal was protected mainly through changing the charge transfer resistance on the metal surface in the tenth day, and the cathodic polarization potential was more negative, the effect was better. The corrosion products were more and poor adhesion on the metal with no-cathodic polarization, and the corrosion products were less and strong adhesion on the metal surface with cathodic protecting. The cathodic polarization could indeed protect the X80 steel in the presence of SRB. In the fifth day, the protection degree was not up to 85% when the metal was polarized to -850 mV_CSE, and it just could meet the protection requirement while polarized to -950 mV_CSE. And in the tenth day the protection degree was declined, it did not meet the requirement while polarized to -850 mV_CSE and -950 mV_CSE. So it was needed to continue to determine the appropriate cathodic protection potential in the presence of SRB.

导出引用

丁清苗, 范玥铭, 张迎芳. X80钢在含有SRB的海水溶液中阴极保护准则适用性[J]. 海洋学研究. 2016, 34(3): 19-24 https://doi.org/10.3969/j.issn.1001-909X.2016.03.004

DING Qing-miao, FAN Yue-ming, ZHANG Ying-fang. Study on the cathodic protection criteria applicability of X80 steel in seawater solution containing SRB[J]. Journal of Marine Sciences. 2016, 34(3): 19-24 https://doi.org/10.3969/j.issn.1001-909X.2016.03.004

中图分类号： TG174

参考文献

[1] AECKMAN W V, SCHENK W, PRINZ W. Manual of cathodic protection, electrochemical protection theory and practice[M].Beijing: Chemical Industry Press,2005.
贝克曼WV,施文克W,普林兹W.阴极保护手册:电化学保护的理论与实践[M].北京:化学工业出版社,2005.
[2] ZHAO X, DUAN J, HOU B, et al. Corrosion of mild steel in sea mud containing sulphate reducing bacteria[J]. Canadian Metallurgical Quarterly,2014,53(4):450-454.
[3] MA Guo-guang, FU Jian-mei, CHEN Si-ding. Fault tree analysis of submarine pipeline corrosion factors[C]//International conference on pipelines and trenchless technology.2012.
[4] LIU Feng-ling, ZHANG Jie, SUN Cai-xia, et al. The corrosion of two aluminium sacrificial anode alloys in SRB-containing sea mud[J]. Corrosion Science,2014,83:375-381.
[5] WANG D, WU M, XIE F, et al. Corrosion behavior of X80 pipeline steel in soil environment containing Sulfate-Reducing Bacteria[J]. Manufacturing and Engineering Technology (ICMET 2014),2014:99.
[6] CAO Pan, ZHOU Ting-ting, BAI Xiu-qin, et al.Research progress on corrosion and protection in deep-sea environment[J]. Journal of Chinese Society for Corrosion and Protection,2015,35(1):12-20.
曹攀,周婷婷,白秀琴,等.深海环境中的材料腐蚀与防护研究进展[J].中国腐蚀与防护学报,2015,35(1):12-20.
[7] ZHAO Xiao-dong. Sulfate-reducing bacteria influenced corrosion of marine steel and itscontrol[D]. Qingdao: China Science Research Institute of Marine Research Institute,2007.
赵晓栋.硫酸盐还原菌对海洋用钢腐蚀行为的影响及其控制[D].青岛:中国科学研究院海洋研究所,2007.
[8] CHEN Guang-zhang, WANG Hong-ren. Cathodic protection technology of marine structures[J]. Corrosion and Protection,2008(z1):14-19.
陈光章,王洪仁.海洋结构中的阴极保护防腐蚀技术[J].腐蚀与防护,2008(z1):14-19.
[9] LU Li-ping, ZHANG Ya-jun, XU Ping, et al. The mechanism and control methods of microbiologically induced corrosion on the pipeline[J]. Journal of Chemical & Pharmaceutical Research,2013,5(12):472-475.
[10] PI Zhen-bang, FAN You-jun, HUA Ping, et al. Electrochemical studies on carbon steel corrosion induced by mixed colonies[J]. Corrosion Science and Protection Technology,2002,14(3):165-171.
皮振邦,樊友军,华萍,等.混合菌种对碳钢腐蚀行为的电化学研究[J].腐蚀科学与防护技术,2002,14(3):165-171.
[11] MEN Hong, ZHANG Jing, ZHANG Li-hua, et al. Study on sulfate reducing bacteria (SRB) inducing corrosion in industrial cooling water[J]. Control and Instruments in Chemical Industry,2011,38(7):777-781.
门洪,张静,张丽华,等.工业冷却水中硫酸还原菌诱导腐蚀研究进展[J].化工自动化及仪表,2011,38(7):777-781.
[12] DING Qing-miao, WANG Hui, LÜ Bo-long, et al. Electrochemical study on impact of AC on cathodic protection potential for X70 steel[J]. Corrosion and Protection,2011,32(12):984-987.
丁清苗,王辉,吕亳龙,等.电化学方法研究交流干扰对阴极保护电位的影响[J].腐蚀与防护,2011,32(12):984-987.
[13] LI Zi-li, DING Qing-miao, ZHANG Ying- fang, et al. Optimal cathodicprotection potential for X70 steel with AC interference determined by electrochemical methods[J]. Corrosion & Protection,2010,31(6):436-439.
李自力,丁清苗,张迎芳,等.用电化学方法建立交流干扰下X70钢的最佳阴极保护电位[J].腐蚀与防护,2010,31(6):436-439.